EN ISO 4957 DIN 1.2365 32CrMoV12-28 H10 Hot Work Tool Steel Iron Round Bar Rod

Features:
1. Competitive price
2. Immediate delivery
3. Premium quality
4. Reliable service
5. MOQ: 1 Ton

Chemical Composition:

DIN 1.2365 H10 Hot Work Tool Steel

Similar Grade: DIN 1.2365, H10

Shape: Round, Flat, Square.

Size Range:

Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished

Heat Treatment:

FORGING: Heating for forging must be done slowly and uniformly. Soak through at 1900-2000°F, and reheat as often as necessary, stopping work when the temperature drops below 1650°F. After forging cool slowly in lime, mica, dry ashes or furnace. H10 hot work tool steel should always be annealed after forging.

ANNEALING: Heat slowly to 1550-1650°F, hold until the entire mass is heated through, and cool slowly in the furnace (40°F per hour) to about 1000°F, after which the cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.

SRAIN RELIEVING: stress reliving when desirable to relieve the strains of machining, heat slowly to 1050-1250°F, allow to equalize, and then cool in still air.

HARDENING: Warm slightly before charging into the preheat furnace, which should be operating at about 1400-1500°F. 1.2365 hot work tool steel is a very deep hardening steel, and although oil quenching may be used where maximum hardness is required, air hardening is recommended for most applications. The use of salt bath or controlled atmosphere furnace is desirable to minimize decarburization, and if not available, pack hardening spent pitch temperature employed Annealing is usually in the range of 1800-1900°F.

TEMPERING: Tempering practice may vary with size and application, but is usually performed in the temperature range of maximum secondary hardness or higher double tempering is recommended.

Applications:

Forging dies for steel, mandrels, dies, die holder bolsters and dummy blocks, punches, die inserts, gripper and header dies, hot shears, aluminum die casting dies.

Product Description:

1.2365 Chromium hot work tool steel has excellent resistance to softening at high temperatures. This particular grade is resisitant to thermal fatigue cracking and can be cooled in water for servicing.

 We, Shanghai Unite Steel are committed to integrate engineering steel resources in china and serve the global engineering steel market. Our company has more than 15 years of experience in steel researching, production, managing and sales. And our team mostly are based on and worked in national famous steel enterprise.

In the aspect of resources and information, we have established cooperative and stronger relationship with nearly hundred enterprises, either state-owned or private owned in china, such as: DAYE Special Steel-a famous steel enterprise with the longest steelmaking history; BAO Steel, and Dongbei Special Steel Group-the biggest special steel manufacturer; TPCO, VALIN-largest seamless steel tube production enterprise; What's more, we have built long, deep and close business relationship with dozens of steel companies, Sharing and holding equities with several steel enterprises. Because of the close cooperation with steel companies and our pioneering spirit, which can ensure us stay at the top competition, and ensure our customers get what they really want!