AISI 1020/S20C professional high-quality forged steel rings

C1020 is forged from 2100 – 2300 º F down to a temperature in the region of 1650 – 1750 º F (1150*–1280 º C down to 900 – 950 º C.). The actual forging and finishing temperatures will depend on a number of factors, including overall reduction during forging and complexity of part being forged. Experience alone will determine near exact values for these two parameters. Parts are air cooled after forging.

APPLICATIONS OF AISI 1020

This grade of steel is used for forged motor shafts, hydraulic shafts and pump shafts, as well as machinery parts.

HEAT TREATMENT

A significant amount of this grade of steel is used in the as-forged condition, since it shows good machinability in this condition.

Little is to be gained, at this carbon level, by a quenching treatment.

At this carbon level, annealing after forging may not be necessary, and depending upon the hardness after forging and the complexity of the part being forged, machining may be carried out on the as-forged parts. If parts are of complex shape and hence there are structural variations throughout the part, then normalizing is in order.

ANNEALING

Full annealing of small C1020 forgings is carried out between 1575 and 1650 º F (860 – 900 º C) followed by furnace cooling at 50 º F (10 º C) per hour, to 1300 º F (700 º C) and air cooling.

NORMALIZING

Normalizing is seldom carried out on carbon contents at this level, but may be used prior to surface hardening. The normalizing temperature range for this grade is typically 1650 – 1700 º F (900 – 930 º C) followed by air cooling. When forgings are normalized before, say, carburizing, the upper range of the normalizing temperature is used. When normalizing is the final treatment, the lower temperature range is used.

HARDENING

This grade of steel is not normally subjected to hardening and tempering treatments as the hardness obtained from such treatments would not warrant their being performed. Carburizing might be carried out at 1620 – 1690 º F (880 – 920 º C,) and carbonitriding at 1470 – 1600 º F (800 – 875 º C,)

Hardening of the carburized case would be performed at 1430 – 1500 º F (780 – 820 º C.) followed by a water quench and a tempering treatment at 300 – 400 º F (150 – 200 º C) to improve case toughness with a minimum effect on its hardness. Case hardness values of Rc 60 may be obtained on carburized C1020.

MACHINABILITY

For parts with a diameter less than 2” (50mm) this grade has been found on occasion to show best machinability when normalized. Parts over 2” (50mm) diameter might be machined following forging or rolling.

WELDABILITY

This grade of steel may be welded by all normal methods: low-carbon electrodes are recommended.

Low-hydrogen electrodes are recommended together with preheat at 300 – 500 º F (150 – 260 º C.) to be maintained during welding, Cool slowly and stress relieve where possible.

 We, Shanghai Unite Steel are committed to integrate engineering steel resources in china and serve the global engineering steel market. Our company has more than 15 years of experience in steel researching, production, managing and sales. And our team mostly are based on and worked in national famous steel enterprise.

In the aspect of resources and information, we have established cooperative and stronger relationship with nearly hundred enterprises, either state-owned or private owned in china, such as: DAYE Special Steel-a famous steel enterprise with the longest steelmaking history; BAO Steel, and Dongbei Special Steel Group-the biggest special steel manufacturer; TPCO, VALIN-largest seamless steel tube production enterprise; What's more, we have built long, deep and close business relationship with dozens of steel companies, Sharing and holding equities with several steel enterprises. Because of the close cooperation with steel companies and our pioneering spirit, which can ensure us stay at the top competition, and ensure our customers get what they really want!